Aging of Solution processed perovskite solar cells


In recent years, perovskite (CH3NH3PbI3-XClX) solar cells have been studied steadily due to their potential properties: low-cost processing and possibility to produce large area by low temperature processes. The perovskite film used as light absorber is obtained by solution process and has a crystalline structure. Many different solvents are being developed and gradually adopted for high-performance inorganic-organic hybrid perovskite solar cells. PEDOT:PSS and PC60BM are used as hole transport layer (HTL) and electron transport layer (ETL), respectively. The size of active area is 0.28cm 2. In this study, 9.54% of power conversion efficiency (PCE) is obtained with a saturated current density (Jsc) of 15.03 mA/cm 2. The degradation of the performance of the solar cell is studied with XRD measurements as well as electrical characterizations. The perovskite solar cell performance decreases with aging time (Table 1 and Figure 1a) and XRD data show the growing of the PbI2 peak and a decreasing of the CH3NH3PbI3 (MAPbI3) peak.
Fichier principal
Vignette du fichier
Heejae LEE_JPH2016_.pdf (191.59 Ko) Télécharger le fichier
Origin : Files produced by the author(s)

Dates and versions

cea-02349409 , version 1 (05-11-2019)


  • HAL Id : cea-02349409 , version 1


Heejae Lee, Arthur Marronnier, Denis Tondelier, Sandrine Tusseau-Nenez, Yvan Bonassieux, et al.. Aging of Solution processed perovskite solar cells. 2èmes journées Pérovskites hybrides (JPH2016), May 2016, Rennes, France. ⟨cea-02349409⟩
56 View
14 Download


Gmail Facebook X LinkedIn More