Critical role of the acetylene content and Fe/C ratio on the thickness and density of vertically aligned carbon nanotubes grown at low temperature by a one-step catalytic chemical vapor deposition process - CEA - Commissariat à l’énergie atomique et aux énergies alternatives Access content directly
Journal Articles Nanomaterials Year : 2022

Critical role of the acetylene content and Fe/C ratio on the thickness and density of vertically aligned carbon nanotubes grown at low temperature by a one-step catalytic chemical vapor deposition process

Abstract

The present work explores the role of the carbon source content and the Fe/C ratio on the synthesis of vertically aligned carbon nanotubes (VACNTs) by one-step aerosol-assisted CCVD operated at a medium temperature (615 °C) on aluminum substrates. The main objective was to overcome the limitations of VACNT growth, constituting a drawback for applications requiring thick VACNTs. By using acetylene as carbon feedstock and ferrocene as a catalyst precursor, we demonstrate that when acetylene content is reduced to 1.5 vol%, it is possible to grow VACNT carpets up to 700 µm thick while maintaining constant VACNT growth for a long duration (up to 160 min). The carbon conversion yield is significantly improved when the acetylene content reaches 1.5 vol%. The Al surface roughness also influences VACNT growth. An optimum Fe/C ratio of 0.8 wt.% coupled with a low acetylene content gives the highest growth rate (5.4 µm/min) ever reported for a thermal aerosol-assisted CCVD process operated at such a low temperature. The CNT number density can be controlled by varying the Fe/C ratio, enabling high density growth (e.g., 1.3 × 10$^{11}$ CNT/cm$^2$).
Fichier principal
Vignette du fichier
nanomaterials-12-02338.pdf (10.46 Mo) Télécharger le fichier
Origin Publisher files allowed on an open archive

Dates and versions

cea-03818565 , version 1 (18-10-2022)

Licence

Identifiers

Cite

Antoine Combrisson, Emeline Charon, Mathieu Pinault, Cécile Reynaud, Martine Mayne-L’hermite. Critical role of the acetylene content and Fe/C ratio on the thickness and density of vertically aligned carbon nanotubes grown at low temperature by a one-step catalytic chemical vapor deposition process. Nanomaterials, 2022, 12 (14), pp.2338. ⟨10.3390/nano12142338⟩. ⟨cea-03818565⟩
29 View
32 Download

Altmetric

Share

Gmail Mastodon Facebook X LinkedIn More