Behavior of cr-coated m5 claddings during and after high temperature steam oxidationfrom 800c up to 1500c - CEA - Commissariat à l’énergie atomique et aux énergies alternatives Accéder directement au contenu
Communication Dans Un Congrès Année : 2018

Behavior of cr-coated m5 claddings during and after high temperature steam oxidationfrom 800c up to 1500c

Résumé

One-sided steam oxidation tests have been conducted at various temperatures between 1000 and 1500°C on several facilities on 12-15µm thick Cr-coated M5 claddings. Microstructural observations and micro-chemical analysis have been performed after oxidation and quenching. Some post-quenching ring compression tests have been also carried out to assess the residual strength/ductility of the Cr-coated materials oxidized at High Temperature (HT). It was confirmed that in the 1000-1300°C oxidation temperature range, the oxidation resistance of the coated materials was enhanced, with a significant additional "coping period" at HT before the material became macroscopically brittle during and/or after quenching. The study was then extended to steam oxidation temperatures higher than 1300°C (Design Extension Conditions). Those tests have confirmed that a eutectic reaction occurred between the zirconium-based substrate and the residual metallic Cr coating above 1300°C. For the DEC-type conditions applied, the tested Cr-coated clad segments did not fail upon the final water quenching while some uncoated reference segments did.
Fichier principal
Vignette du fichier
201800002888.pdf (1.87 Mo) Télécharger le fichier
Origine Fichiers produits par l'(les) auteur(s)
Loading...

Dates et versions

cea-02328975 , version 1 (04-12-2019)

Identifiants

  • HAL Id : cea-02328975 , version 1

Citer

J.C. Brachet, T. Guilbert, M. Lesaux, J. Rousselot, G. Nony, et al.. Behavior of cr-coated m5 claddings during and after high temperature steam oxidationfrom 800c up to 1500c. Topfuel 2018, Sep 2018, Prague, Czech Republic. ⟨cea-02328975⟩

Collections

CEA DEN EDF
160 Consultations
228 Téléchargements

Partager

Gmail Mastodon Facebook X LinkedIn More