%0 Journal Article %T Is glass brittle at all scales? %T Le verre est-il fragile à toutes les échelles ? %+ Service de physique de l'état condensé (SPEC - UMR3680) %+ Institut de Recherche de Chimie Paris (IRCP) %A Bouchaud, Élisabeth %Z Prix Aniuta Winter-Klein 2013 de l’Académie des sciences %< avec comité de lecture %@ 1631-0705 %J Comptes Rendus. Physique %I Académie des sciences (Paris) %V 15 %P 527 - 535 %8 2014 %D 2014 %R 10.1016/j.crhy.2014.06.002 %K Stress corrosion cracking %K Quasi-brittle fracture %K Damage %K Silicate glas %Z Physics [physics]Journal articles %X Quasi-brittle fracture Damage Silicate glass Mots-clés : Corrosion sous contrainte Rupture quasi fragile Endommagement Verre de silice Although silicate glass is considered as the archetype of brittle materials, which break without deforming irreversibly, its fracture involves some dissipation. By examining the post-mortem fracture surfaces, by following in situ the progression of a stress corrosion crack and by measuring the depth of penetration of water in the material during slow fracture, we show that glass behaves in fact in a quasi-brittle manner, with a damaged zone of ∼10 nm developing ahead of the crack tip. %X Bien que le verre de silice soit considéré comme l'archétype des matériaux fragiles, qui cassent sans se déformer, sa rupture s'accompagne de dissipation. Par l'examen post-mortem de surfaces de rupture, le suivi in situ de la progression d'une fissure de corrosion sous contrainte et la mesure de la profondeur de pénétration de l'eau dans le matériau pendant sa fissuration lente, nous montrons que le verre se comporte en fait de manière quasi fragile, avec une zone endommagée d'une dizaine de nanomètres qui se développe en pointe de fissure. %G English %L cea-01377317 %U https://cea.hal.science/cea-01377317 %~ CEA %~ ENSCP %~ CNRS %~ ENSC-PARIS %~ PARISTECH %~ INC-CNRS %~ IRAMIS-SPEC %~ PSL %~ ENSCP-PSL %~ IRAMIS %~ GS-PHYSIQUE %~ TEST2-HALCNRS